Feature: | EVA |
---|---|
CAS No.: | 24937-78-8 |
Formula: | (C2h4)X.(C4h6o2)Y |
EINECS: | 607-457-0 |
Material: | Ethylene-Vinyl Acetatecopolymers/EVA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Samples: |
---|
Suppliers with verified business licenses
EVA16%
PROPERTIES
|
TEST METHOD
|
UNIT
|
Data
|
VA Content
|
|
%
|
16.0
|
Density
|
ASTM D1505
|
g/cm3
|
0.937
|
Melt Index MI2.16
|
ASTM D1238
|
g/10min
|
1.5
|
Tensile Strength (Break)
|
ASTM D638
|
Kg/cm2
|
170
|
Elongation at break
|
ASTM D638
|
%
|
700
|
Melting point
|
ASTM D-3418
|
ºC
|
89
|
Hardness
|
ASTM D2240
|
Shore D
|
37
|
Properties
|
Test method
|
Value
|
VA Content(%)
|
USI
|
18
|
Density(g/cm3)
|
ASTM D792
|
0.939
|
Melt Index (g/10min)
|
ASTM D1238
|
2.5
|
Tensile Strength(Molded)(Break)(kg/cm2)
|
ASTM D638
|
180
|
Ultimate elongation(Molded)(%)
|
ASTM D638
|
750
|
Low Temperature Brittleness(ºC/F50)
|
ASTM D746
|
<-76
|
Vicat Softening Point(ºC)
|
ASTM D1525
|
64
|
Melt Point (ºC)
|
ASTM D3418
|
86
|
Hardness(Shore D)
|
ASTM D2240
|
36
|
PROPERTIES
|
TEST METHOD
|
UNIT
|
Data
|
VA Content
|
|
%
|
28.0
|
Density
|
ASTM D1505
|
g/cm3
|
0.954
|
Melt Index MI2.16
|
ASTM D1238
|
g/10min
|
15
|
Tensile Strength (Break)
|
ASTM D638
|
Kg/cm2
|
80
|
Elongation at break
|
ASTM D638
|
%
|
>800
|
Melting point
|
ASTM D-3418
|
ºC
|
69
|
Hardness
|
ASTM D2240
|
Shore D
|
20
|